| STANDARTS | CLASSIFICATIONS | |||||||||||||||||
| TS EN ISO 14343-A | G 18 8 Mn | |||||||||||||||||
| AWS A5.9 | ER 307Si | |||||||||||||||||
| SPECIFICATIONS AND APPLICATION FIELDS | ||||||||||||||||||
Austenitic stainless steel wire electrode for gas metal arc (MIG/MAG) welding of dissimilar steels, low-weldability steels, armor steels, high-manganese (Mn) steel castings, rails, and trusses. It is well-suited for welding crack-sensitive parts, such as crane bandages, and for stress-relieving buffer layer welds prior to hardfacing. The weld metal is resistant to corrosion and operating temperatures up to 300°C and to scaling up to 850°C. Attention should be paid to the welding procedure, preheating temperatures, and dilution ratio of the base metal. |
||||||||||||||||||
| CHEMICAL PROPERTIES OF WELDING WIRE | ||||||||||||||||||
| ANALYSIS TYPE | C | Sİ | MN | CR | Nİ | |||||||||||||
| WELDING WIRE | 0,045 | 0,81 | 6,37 | 18,72 | 8,05 | |||||||||||||
| MECHANICAL PROPERTIES OF WELDING WIRE | ||||||||||||||||||
TEST TYPE |
SHIELDING GAS |
YIELD STRENGTH (MPA) |
TENSILE STRENGTH (MPA) |
ELONGATION (%) |
NOTCH IMPACT RESISTANCE ISO-V(- 40℃) |
|||||||||||||
AFTER WELDING |
M12-M13-M14 | MİN 400 | MİN 580 | MİN 30 | MİN 63 J | |||||||||||||
| WELDING POSITIONS | ||||||||||||||||||
 |
||||||||||||||||||
| SHIELDING GAS | POLARIZATION | |||||||||||||||||
| M12-M13-M14 |  |
|||||||||||||||||
| PACKAGING INFORMATION | ||||||||||||||||||
| DIAMETER (MM) |
PACKAGING TYPE |
NET WEIGHT OF 1 PIECE (KG ) |
||||||||||||||||
| 1,00 | METAL SPOOL | 15 | ||||||||||||||||
| 1,20 | METAL SPOOL | 15 | ||||||||||||||||